APMS Zirconia Block Multilayer

Features:
The production level integrating several patented technologies in one all the while meeting the full range of indication. It has larger systematic processing, a wider sintering temperature range, and a increased stable
three-dimensional gradient effect.

Incisal layer
53% Translucency 700MPa

Cervical layer
43% Translucency 1050MPa

2 hours
On the basis of realizing rapid sintering, APMS is compatible with many kinds of zirconia materials (such as HTC,HTW) to achieve simultaneous sintering of multiple materials.

1510-1570
ultra-wide sintering temperature range, giving a perfect bionic aesthetic effect at different temperatures.

Color:A1/A2/A3/A3.5/A4/B1/B2/B3/B4/C1/C2/C3/C4/D2/D3/D4/OM1/OM2/OM3
Aesthetic:Super high translucency
Sintered density: ≥6.0g/cm³
Bending strength:Cervical part 1050MPa
Fracture toughness: 5Mpam^0.5
Hardness (Hv10):1250

98mm

Mechanical property
Veneer,Inlay,Anterior crown,Posterior crown,
Full arch crown bridge,Full crown bridge,
Full contour screw retained bridge,lmplant

S699 Dental Plastic Precision Rod Attachments

ROD-Attachments
The male is made of burn out plastic and can be therefore cast in nearly every alloy. The female is made of a highly elastic and precise acrylic material. The female is exangeable.
Advantages
•paralleling mandrel is placed to the patrix rod
•females are easy to replace
•females are available with different interior diameters for individual friction
•inexpensive attachment for partial denture
•castable or solderable INOX sleeves guarantee exact positioning of the females
69977  Male,blue
86378  Female,yellow,rigid